Investigating the effect of electrolyte types with various ionic liquids on the electrochromic performance of PEDOT:PSS based LbL multilayers


Okutan M., Evecan D., Yildirim S., Zayim E., DELİGÖZ H.

MICROELECTRONIC ENGINEERING, cilt.234, 2020 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 234
  • Basım Tarihi: 2020
  • Doi Numarası: 10.1016/j.mee.2020.111454
  • Dergi Adı: MICROELECTRONIC ENGINEERING
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus, Academic Search Premier, PASCAL, Aerospace Database, Chemical Abstracts Core, Communication Abstracts, Compendex, INSPEC, Metadex, Civil Engineering Abstracts
  • İstanbul Üniversitesi Adresli: Evet

Özet

The objective of the study is to investigate the electrochromic performances of layer-by-layer (LbL) multilayered thin film electrode prepared from linear polyethylene imine (LPEI) and poly(3,4-ethylenediox-ythiophene):polystyrene sulfonate (PEDOT:PSS) on PET-ITO substrate in the presence of different types of electrolytes. For this purpose, the electrochromic behaviors of (LPEI/PEDOT:PSS) 10 is performed in LiClO4/propylene carbonate (PC) and two different ionic liquids (IL) namely N-methylimidazolium tetrafluoroborate (Melm-BF4) and 2-hydroxy ethyl ammonium formate (2-HEAF), as a function of IL content and scanning rate. The optical contrast value of (LPEI/PEDOT:PSS) 10 film is determined as 58.4% in the existence of 10 wt% of 2-HEAF as the electrolyte. The coloration efficiency of this film is determined as 606.7 cm(2)/C, which this value was greater approximately four times than 1 M LiClO4/PC. According to the obtained results, 2-HEAF has been evaluated as a suitable electrolyte alternative for (LPEI/PEDOT:PSS) 10 film due to its better optical contrast and coloration efficiency compared to other electrolytes.