The Effect of Desulfovibrio sp Biofilms on Corrosion Behavior of Copper in Sulfide-Containing Solutions


Gungor N. , Cotuk A., Dışpınar D.

JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, cilt.24, ss.1357-1364, 2015 (SCI İndekslerine Giren Dergi) identifier identifier

  • Cilt numarası: 24 Konu: 3
  • Basım Tarihi: 2015
  • Doi Numarası: 10.1007/s11665-015-1388-2
  • Dergi Adı: JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
  • Sayfa Sayıları: ss.1357-1364

Özet

This study aims to detect the effect of Desulfovibrio sp. on copper in terms of biofilm formation and corrosion in 722 h. In that way, appropriate strategies to inhibit microbiological corrosion in copper systems with Desulfovibrio sp. can be evaluated. For this purpose, experiments were performed in 1 L glass model system containing 28 copper coupons and pure culture of the sulfate-reducing bacteria (SRB) strain Desulfovibrio sp. in Postgate's medium C. Also, a control system with copper coupons but without Desulfovibrio sp. containing sterile Postgate's medium was studied concurrently with the test system. The test coupons were collected from systems at certain time intervals, namely 24, 168, 360, and 720 h. The samples were then subjected to several characterization analyses such as measurement of Desulfovibrio sp. numbers, corrosion resistance, EPS extraction, carbohydrate analysis, SEM, and EDS. During the experiments, the maximum Desulfovibrio sp. count in biofilm samples was found at 360 h. Carbohydrate and copper concentrations in biofilm were increased over time. EDS analysis revealed Cu, S, C, O, and Cl peaks on the surface of the samples. For the control coupons, only Cu peaks were observed. The results obtained from this study showed that copper was corroded by Desulfovibrio sp. in the model system under laboratory conditions.