Thermodynamic analysis and effect of temperature on surface hardening of tungsten heavy alloys using ethanol


Cetinkaya S., Eroğlu S.

JOURNAL OF ALLOYS AND COMPOUNDS, cilt.632, ss.161-164, 2015 (SCI-Expanded) identifier identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 632
  • Basım Tarihi: 2015
  • Doi Numarası: 10.1016/j.jallcom.2015.01.211
  • Dergi Adı: JOURNAL OF ALLOYS AND COMPOUNDS
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Sayfa Sayıları: ss.161-164
  • İstanbul Üniversitesi Adresli: Evet

Özet

Surface hardening of 92.5W-5.25Ni-2.25Fe (wt.%) heavy alloy was investigated at 1200-1500 K using ethanol as carbon source. The hardened surfaces were characterized by XRD, optical microscope and microhardness tester. Microhardness of the alloy increased from HV0.3 318 to 1640 with temperature. This was attributed to both increased thickness of WC shells formed on W grains and increased reaction depth as a result of higher C diffusion. Reaction pathways leading to WC formation were explained using thermodynamic and experimental results. (C) 2015 Elsevier B.V. All rights reserved.