JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, cilt.30, sa.7, ss.1813-1826, 2017 (SCI-Expanded)
In this study, Y3+ ion-substituted M-type barium hexaferrites (BaM; BaFe12O19) were fabricated via facile ceramic route. As-prepared powders were characterized by X-ray powder diffractometry (XRD), Fourier transform infrared (FT-IR) spectroscopy, and impedance spectroscopy. XRD (Rietveld) analyses confirmed the presence of a single characterization of all samples (except x = 0.0 and 0.1 samples). The crystallite sizes of products are found in the range of 47.2-63.2 nm. Spectral analysis (FT-IR) also presented the formation of spinel structure for all products. The ac conductivity of the substituted samples was found to initially decrease slightly with increase in Y3+ compared with unsubstituted, and then variation tendency changes at the medium substitution ranges are observed with a different attitude against temperature. In the end, the lower conductivity for high substitutions is recorded and increases as functions of frequency while it also increases with the elevation of temperature. It was observed that ac conductivities of products increased by increasing frequency which indicate that observed ac conductivity is due to both electronic and polaron hopping mechanism.