The Effect of TiO2 and B2O3 Additions on the Grain Growth of ZnO


Hardal G., Price B.

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, sa.4, ss.2090-2098, 2017 (SCI-Expanded) identifier identifier

Özet

The microstructure properties and grain growth kinetics of ZnO-B2O3-TiO2 ceramics with 0.5 and 1 mol pct doping of TiO2 were investigated. The samples were sintered at 1373 K, 1473 K, and 1573 K (1100 A degrees C, 1200 A degrees C, and 1300 A degrees C) for 1, 2, and 3 hours. The bulk density and grain size of ZnO samples increased with the addition of B2O3 and TiO2. The grain size of 0.5 mol pct TiO2-doped ZnO ceramics was larger than the grain size of the 1 mol pct TiO2-doped ZnO ceramics. This is due to the increase in the ZnTi2O4 phase for the 1 mol pct TiO2-doped ZnO ceramics. The value of grain growth kinetic parameters (n and Q) increased when the TiO2 content in ZnO ceramics increased from 0.5 to 1 mol pct. The lowest n and Q values were obtained for the 0.5 mol pct B2O3-doped ZnO samples which showed that the addition of B2O3 has a significant role on the grain growth of ZnO ceramics.