Electrical properties of high temperature insulation coatings under various pressures at 298 K and 77 K

Cakiroglu O., Arda L.

6th International Conference of the Balkan-Physical-Union, İstanbul, Türkiye, 22 - 26 Ağustos 2006, cilt.899, ss.431-432 identifier identifier

  • Yayın Türü: Bildiri / Tam Metin Bildiri
  • Cilt numarası: 899
  • Doi Numarası: 10.1063/1.2733221
  • Basıldığı Şehir: İstanbul
  • Basıldığı Ülke: Türkiye
  • Sayfa Sayıları: ss.431-432
  • İstanbul Üniversitesi Adresli: Evet

Özet

The high temperature insulation coatings were prepared using solution of Mg and Zr based precursors. Then the MgO-ZrO2 coating was applied on long-length Stainless-Steel tapes using a non-vacuum reel-to-reel sol-gel dip coating technique. The thicknesses of coatings 7, 12 and 15 mu m for 4, 8 and 12 dip, respectively. Three different types of stycast, 2850 FT/24 LV Black and Blue, and White Buechler Epoxide Resin were studied. Stycast thicknesses were varied from 32-18 mu m, when pressure was applied from 0 to 0.54 GPa. Electrical properties of the coated tapes were investigated under various pressures at room temperature (298K) and in liquid nitrogen (77K).